{"product_id":"effect-of-ni-and-si-addition-to-al-8si-0-4mg-alloy-von-nidhin-raj","title":"Effect of Ni and Si Addition to Al-8Si-0.4Mg Alloy","description":"\u003cp\u003eAn investigation is being carried out to determine the effect of varying Ni content on the Al-8Si-0.4Mg alloy and the effect of varying Si content on the Al-0.4Mg-Si-2Ni alloy. The following mechanical properties are studied: 1.Microstructure. 2. Hardness. 3. Tensile properties (ultimate tensile strength (UTS), yield strength (YS), % elongation (%EL)) 4. Wear rate. 5. CoF (Coefficient of friction) and 6.Hot tensile properties (UTS, YS, % EL). The type of the intermediate phase that forms during solidification in the Ni added and Si added alloys is investigated in this study. The Al-8Si-0.4Mg base alloy was melted in an electric furnace and Ni was added to the melt in the appropriate amount (2, 4, 6, 8 and 10 wt %). Similarly the Al-0.4Mg-Si-2Ni alloy was melted and Si was added to the melt in the appropriate amount (4, 8, 12 and 16 wt%). The melt was cast in a metal mould. Test specimens were solutionised at 537°C for 12 hrs. The water quenched specimens were then aged at 155°C for 3 hrs.\u003c\/p\u003e\u003cdiv class=\"aw-variant-hidden-subtitle-div\" id=\"aw-variant-subtitle-9786139836437\"\u003e\u003ch3\u003e\u003c\/h3\u003e\u003c\/div\u003e","brand":"Libri","offers":[{"title":"Softcover - 9786139836437","offer_id":39455097520221,"sku":"9786139836437","price":61.9,"currency_code":"EUR","in_stock":true}],"thumbnail_url":"\/\/cdn.shopify.com\/s\/files\/1\/0940\/0622\/files\/2eeb8b60-3615-40f9-a384-abbf4c68859e.jpg?v=1770791878","url":"https:\/\/shop.autorenwelt.de\/products\/effect-of-ni-and-si-addition-to-al-8si-0-4mg-alloy-von-nidhin-raj","provider":"Autorenwelt Shop","version":"1.0","type":"link"}